Spin coated (Mx, Zn1-x O), M= Sn, Al nanofibers investigation
1 Physics Department, Sciences Faculty, USTOMB University, BP1505 Oran, Algeria
2 ITT- DIEE, Apdo, Postal 20, Metepec 3, 52176, Estado de Mexico, Mexico
3 Department of Science, Faculty of Education, University of Dicle, 21280 Diyarbakir, Turkey
a e-mail: bmost_31@yahoo.fr
(Mx, Zn 1-x O), M= Sn, Al nanofibers properties were investigated. Pure and M-doped zinc oxide films were fabricated onto a glass substrate by a facile and low cost spin coating route. X-rays analysis reveals that films crystallize with a wurtzite structure according to (002) orientation. The transmittance in the visible range was as high as 88 % at 550 nm. The doping increased slightly the transmittance, the as-grown films were high transparent in VIS and IR ranges. The optical band gap was a little bit changed by doping. AFM 3D-views revealed that grains were nanofibers with the size of 18.22, 18.23 and 44.27 nm respectively for pure, Al and Sn-doped ZnO films.
© Owned by the authors, published by EDP Sciences, 2013
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.