Dynamic behavior of zirconium alloy E110 under submicrosecond shock-wave loading
RFNC-VNIITF, 456770, Snezhinsk, Chelyabinsk region, Russia
a Corresponding author: firstname.lastname@example.org
Published online: 7 September 2015
Stress waves have been measured under shock wave loading of zirconium alloy E110 samples with the 0.5 – 8 mm thickness at normal and elevated temperatures. Duration of shock loading pulses varied from ∼0.05 up to 1μs with the amplitude varying from 3.4 up to 23 GPa. Free-surface velocity profiles have been registered using VISAR and PDV interferometers with nanosecond resolution. Attenuation of the elastic precursor has been measured to determine plastic strain rate behind the elastic precursor front. The plastic strain rate was observed to decrease with propagation from 106 s−1 at the 0.46-mm distance down to 2 ⋅ 104 s−1 at the 8-mm distance. Spall strength has been measured under normal and elevated temperatures. Spall strength versus strain rate relationships have been constructed in the 105 s−1 – 106s−1 range. Under shock compression higher than 10.6 GPa, the three-wave configuration of the shock wave has been registered and the polymorphous α → ω transition is considered to be the reason of this phenomenon. This work was supported by State Atomic Energy Corporation “Rosatom” within State Contract # H.4x.18.104.22.1681
© Owned by the authors, published by EDP Sciences, 2015
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.