The optimal composition of reagents for producing aluminosilicate glue based on fly ash of thermal power plants
1 T.F. Gorbachev Kuzbass State Technical University, Department of Heat Power Engineering, 650000 Kemerovo, 28 Vesennya st., Russian Federation
2 Kutateladze Institute of Thermophysics SB RAS, 630090 Novosibirsk, 1 Ak. Lavrent’eva ave., Russian Federation
* Corresponding author: email@example.com
Published online: 14 January 2019
The work is devoted to the processing of fly ash wastes obtained from coal combustion. Based on the non-magnetic fraction of fly ash (its particle size of 0-50 μm), an aluminosilicate glue or liquid glass as a cementing component has been obtained. It was represented by a number of silicate modules (SiO2/Me2O molar ratios): 2, 2.5 and 3 (for three different formulations). The shear deformation tests for glued plates with glues of various silicate modules have been carried out. The shear stresses for the samples with silicate modules of 2.0, 2.5, 3.0 were equal to 48, 66 and 34 kPa, respectively. These results suggest that during the production of aluminosilicate glue, the silicate module of 2.5 is more favored for providing the strongest bond between ceramic tiles.
© The Authors, published by EDP Sciences, 2019
This is an Open Access article distributed under the terms of the Creative Commons Attribution License 4.0, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.